3032584 
Journal Article 
Mechanical properties of micro and sub-micron wollastonite fibers in cementitious composites 
Dey, V; Kachala, R; Bonakdar, A; Mobasher, B 
2015 
Yes 
Construction and Building Materials
ISSN: 0950-0618
EISSN: 1879-0526 
82 
351-359 
WOS:000353090200036 
Effect of mineral wollastonite micro and sub-micron fibers on the mechanical properties of cement-based systems are studied using compressive strength and notched beam flexural tests. A series of blended paste and mortar mixtures with silica fume and wollastonite particles of different morphology and size were developed and tested. Testing variables included four grades of wollastonite fibers or platelets with average particle size ranging from 33 to 2000 pm, with aspect ratios varying from 3:1 to 20:1, and cement replacement levels of 5%, 10%, and 15%, by mass. Non-linear fracture mechanics concepts used indicate considerable effect of wollastonite reinforcement on the fracture resistance of the cementitious matrix. Uniaxial compressive strength tests showed a 30% increase due to 10% cement replacement with wollastonite and silica fume. Flexural strength was enhanced by 40% and fracture toughness by as much as 150% at the optimal dosage of wollastonite fibers. Morphology of fractured surfaces was studied using SEM to correlate the mechanical properties with internal micro-structure. It was observed that at optimal dosage, wollastonite fibers promote classical toughening mechanisms such as crack bridging and crack path deflection. (C) 2015 Published by Elsevier Ltd. 
Fiber-reinforced concrete; Wollastonite; Fiber; Micro-fiber; Fracture; R-Curves; Toughness