Determination of the glass transition temperature of latex films: Comparison of various methods 
Backfolk, Kai; Holmes, Rob; Ihalainen, P; Sirvioe, P; Triantafillopoulos, N; Peltonen, J 
2007 
1 
Polymer Testing
ISSN: 0142-9418
EISSN: 1873-2348 
26 
8 
1031-1040 
WOS:000251752600007 
The glass transition temperature (Tg) for two latices with different styrene/butadiene compositions was determined by the thermal SPM probe resonance frequency method. The results were compared with the Tg values obtained by differential scanning calorimetry (DSC), dynamical mechanical analysis (DMA), process rheometer (PR) and thermo-mechanical analyzer (TMA) measurements. The Tg values detected by the thermal SPM method agreed well with the Tg values obtained by DSC and calculated by the Fox–Flory equation. DMA, on the other hand, showed a significantly higher Tg value for both latices than those obtained from theoretical calculations, the thermal SPM method and DSC. The Tg obtained from the PR curve was slightly higher for the latex with a low styrene content, whereas good agreement was obtained with the thermal SPM data for the latex with a high styrene content. The glass transition temperature determined by TMA agreed fairly well with the thermal SPM data for the latex with the low styrene content, whilst the value of Tg for the second latex was much less than those obtained by the other methods. The thermal SPM method detects changes in thermal behavior (thermal diffusivity, heat capacity) during heating of the latex films rather than changes in the mechanical properties. Information about the sample history could be seen in the thermal SPM curves, which was further associated with the degree of latex film formation, especially when the roughness of the films was taken into consideration. 
DSC; AFM; DMA; PR; TMA; glass transition temperature; phase transition; styrene; butadiene; latex; film