Topçu, İB; Toprak, MU; Akdağ, D
Microwave energy can accelerate the hydration of cement, which results in the rapid strength development of concrete. In this paper, prediction of later age compressive strength of fly ash cement mortars, based on the accelerated strength of mortars cured with microwave energy, was investigated. To accelerate curing properly, optimal processing parameters of microwave curing (MC) on Portland cement mortars (CM) and fly ash cement mortars (FA) were first determined and then were applied to mortars. The possible early ages for the strength prediction were found to be at 6 and 8 h for CM and FA, respectively. The error percentages for prediction of CM were ±2.22% and 2.91% for 7 and 28 d, respectively. Error percentages for FA, on the other hand, were ±4.36% and 5.20% for 7 and 28 d, respectively. (English) [ABSTRACT FROM AUTHOR] L’énergie micro-onde peut accélérer l’hydratation du ciment, ce qui engendre le développement rapide de la résistance du béton. Le présent article examine la prévision de la résistance en compression àun âge plus avancé des mortiers de ciment contenant des cendres volantes par rapport àla résistance accélérée des mortiers durcis par micro-ondes. Afin d’accélérer adéquatement le durcissement, il fallait d’abord déterminer les paramètres optimaux de traitement de durcissement par micro-ondes (« MC ») sur les mortiers de ciment Portland (« CM ») et les mortiers de ciment contenant des cendres volantes (« FA ») puis les appliquer aux mortiers. Les âges précoces possibles de la prévision de résistance ont été de 6 et de 8 heures respectivement pour « CM » et « FA ». Les pourcentages d’erreur de prévision des « CM » étaient respectivement de ±2,22 % et de 2,91 % pour 7 et 28 jours; par contre, les pourcentages d’erreur des « FA » étaient respectivement de ±4,36 % et de 5,20 % pour 7 et 28 jours. (French) [ABSTRACT FROM AUTHOR] Copyright of Canadian Journal of Civil Engineering is the property of NRC Research Press and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts)
RADIATION curing; FLY ash; PORTLAND cement; HYDRATION; CEMENT -- Effect of temperature on; MICROWAVE pressing; CEMENT plants; ERROR rates; INDUSTRIAL efficiency; accelerated curing; microwave curing; mortar; strength prediction; durcissement accéléré; durcissement par micro-ondes; mortier; prévision de la résistance