COLORIMETRIC DETERMINATION OF IRON(II) AND IRON(III) IN GLASS 
Baumann, EW; , 
1992 
1 
Analyst
ISSN: 0003-2654
EISSN: 1364-5528 
ROYAL SOC CHEMISTRY 
CAMBRIDGE 
913-916 
WOS:A1992HU71100016 
A simple method to determine relative amounts of Fe(II) and Fe(III) was developed for the analysis of glass containing nuclear waste. The pulverized glass sample was dissolved in a sulfuric acid-hydrofluoric acid mixture with ammonium metavanadate added to preserve the Fe(II) content. The V(V)-V(IV) couple, which is strongly acid-dependent, caused the Fe(II) to be oxidized to Fe(III) in the highly acidic dissolution and then to be regenerated when the solution was adjusted to pH 5 for formation of the magenta Fe(II)-Ferrozine complex. Boric acid was added to complex the fluoride and permit regeneration of Fe(II), otherwise Fe(III) would be stabilized as a fluoride complex. The Fe(II) content was determined from the absorbance at 562 nm, and total Fe was determined from the absorbance of the same solution after ascorbic acid had been added to reduce Fe(III) to Fe(II). The relative standard deviation was 5%, and the range was 3-97% for Fe(II) in total Fe. The method was validated by analysing a glass frit spiked with ammonium iron(II) sulfate and/or ammonium iron(III) sulfate solutions. The method is applicable to glasses (or minerals) that contain more than about 5% total Fe.