Temperature-controlled synthesis of spinel lithium nickel manganese oxide cathode materials for lithium-ion batteries 
Lee, B; Chu, CT; Krajewski, M; Michalska, M; Lin, JYu; , 
2020 
1 
Ceramics International
ISSN: 0272-8842
EISSN: 1873-3956 
ELSEVIER SCI LTD 
OXFORD 
46 
13 
20856-20864 
WOS:000556283900026 
In this work, we successfully synthesized series of LiNi0.5Mn1.5O4 (LNMO) cathode materials with spinel structure by using a facile sol-gel method and then calcined at various temperature ranging from 600 to 1000 degrees C. The application of different calcination temperatures significantly influenced the surface morphology, stoichiometry and crystalline nature of the as-synthesized LNMO material. According to the results of physical characterizations, the LNMO materials calcined at various temperatures mainly revealed the stoichiometric disordered Fd-3m structure with a small amount of well-ordered P4(3)32 phase. The structural analysis also exhibited that the control of the calcination temperature contributed to the higher crystalline nature. Moreover, the morphological investigations indicated that the increasing calcination temperatures caused the formation of large micron-sized LNMO material. In turn, the electrochemical evaluations revealed the impact of the calcination temperatures on enhancing the electrochemical performances of the LNMO electrode materials up to 900 degrees C. The LNMO electrode calcined at 900 degrees C exhibited an impressive initial discharge specific capacity of ca. 142 mAh g(-1) between 3.5 and 4.9 V vs. Li/Li+ , and remarkably improved capacity retention of 97% over 50 cycles. Those excellent electrochemical properties were associated with the presence of the dominant Fd-3m phase over the P4(3)32 phase. Additionally, the results of the corrosion and dissolution tests which were performed for all calcined LNMO materials in order to estimate the amount of manganese and nickel ions leached from them, proved that the micro-sized LNMO calcined at 900 degrees C was the most stable. 
Spinel LiNi0.5Mn1.5O4; Sol-gel synthesis; Calcination temperature; Cathode material; Lithium-ion batteries